(n = 5 spots/disc and tip)
|
Ti
|
Zr
|
O
|
C
|
fe %
|
te
|
|---|
|
Disc I
|
|
0
|
88.0 ± 13.6
|
0
|
5.4 ± 4.8
|
6.1 ± 8.5
|
Al 9.9
|
Ca, Si
|
|
A
|
83.0 ± 16.2
|
0
|
6.4 ± 2.1
|
1.5 ± 0.2
|
Fe 39.1, Cr 5.4
|
-
|
|
B
|
80.7 ± 18.3
|
0
|
9.3 ± 5.1
|
9.6 ± 15.3
|
-
|
Al, Ca, Si, Fe
|
|
C
|
86.1 ± 8.6
|
0
|
10.5 ± 5.8
|
3.1 ± 2.6
|
-
|
Si, Ca
|
|
D
|
78.1 ± 24.0
|
0
|
18.1 ± 20.5
|
12.0 ± 18.3
|
S 8, Ca 3
|
-
|
|
E
|
63.1 ± 31.7
|
0
|
7.2 ± 4.3
|
27.7 ± 26.5
|
S 6
|
Ca
|
|
Disc II
|
|
0
|
73.3 ± 11.5
|
12.9 ± 2.9
|
9.2 ± 9.2
|
8.7 ± 11.1
|
-
|
S, Ca
|
|
A
|
56.5 ± 6.6
|
12.6 ± 0.4
|
8.3 ± 5.2
|
1.9 ± 0.7
|
-
|
-
|
|
B
|
71.0 ± 15.8
|
12.1 ± 3.3
|
8.1 ± 6.3
|
8.3 ± 11.7
|
-
|
Ca, Al, S, Na, Si
|
|
C
|
78.2 ± 4.5
|
13.3 ± 0.7
|
6.8 ± 3.7
|
1.7 ± 0.9
|
-
|
-
|
|
D
|
62.3 ± 30.9
|
10.9 ± 5.5
|
6.2 ± 2.0
|
14.6 ± 24.2
|
-
|
-
|
|
E
|
38.1 ± 35.7
|
6.9 ± 6.6
|
6.2 ± 4.9
|
44.2 ± 33.6
|
S 14.0
|
Si, Ca
|
|
Disc III
|
|
0
|
74.7 ± 16.7
|
0
|
16.5 ± 9.5
|
2.7 ± 1.5
|
Al 27
|
Ca, Si
|
|
A
|
84.6 ± 9.9
|
0
|
9.0 ± 4.0
|
1.9 ± 0.7
|
Fe 9.8, Al 10.3, Cr 1.5
|
-
|
|
B
|
73.7 ± 19.2
|
0
|
10.8 ± 4.6
|
12.6 ± 15.2
|
Al 9.5
|
Ca, Si
|
|
C
|
88.5 ± 5.1
|
0
|
8.8 ± 4.0
|
1.9 ± 0.5
|
Al 5.7,
|
Si
|
|
D
|
58.1 ± 17.7
|
0
|
19.4 ± 10.3
|
12.8 ± 15.9
|
S 13, Ca 12, Al 5, Si 2.0
|
-
|
|
E
|
44.2 ± 35.4
|
0
|
17.9 ± 10.5
|
21.4 ± 23.3
|
Al 51, S 6
|
Ca, Na, Si
|
|
Disc IV
|
|
0
|
77.7 ± 2.7
|
13.9 ± 1.9
|
7.1 ± 10.2
|
3.3 ± 1.4
|
-
|
-
|
|
A
|
78.8 ± 5.3
|
12.3 ± 2.2
|
6.0 ± 3.7
|
1.7 ± 1.6
|
Fe 3.2
|
-
|
|
B
|
79.4 ± 2.2
|
12.9 ± 0.8
|
5.4 ± 2.1
|
2.3 ± 0.5
|
-
|
-
|
|
C
|
77.0 ± 4.9
|
14.5 ± 2.8
|
5.2 ± 1.7
|
3.1 ± 1.6
|
-
|
Fe, Ca
|
|
D
|
77.4 ± 3.5
|
12.9 ± 1.2
|
7.3 ± 3.3
|
2.4 ± 1.0
|
-
|
-
|
|
E
|
73.0 ± 13.4
|
35.0 ± 44.2
|
3.9 ± 0.5
|
7.6 ± 9.7
|
-
|
Ca, S, B
|
- Disc I—Inicell, Disc II—SLA, Disc III—non pretreated, Disc IV—machined
- 0—non instrumented surface, A—steel, B—PEEK, C—titanium, D—Carbon, E—resin
- Ti—Titanium, Zr—zirconium, O—oxygen, C—carbon, fe—foreign metals > 1.0%, te—traces of foreign elements